China (Mainland)
Hydrogenation catalyst for prehydrogenation of high sulphur reforming material CAS NO.64742-16-1
- FOB Price: USD: 4.89-4.89 /Kilogram Get Latest Price
- Min.Order: 1000 Kilogram
- Payment Terms: L/C,T/T
- Available Specifications:
industry grade(1000-10000)Kilogram
- Product Details
Keywords
- Hydrogenation catalyst
- catalyst
- r prehydrogenation of high sulphur reforming material
Quick Details
- ProName: Hydrogenation catalyst for prehydrogen...
- CasNo: 64742-16-1
- Molecular Formula: RhCl[P(C6H5)3]
- Appearance: Trilobe extrudates
- Application: It is mainly used for prehydrogenation...
- DeliveryTime: Negotation
- PackAge: Packing: iron drums innerlining double...
- Port: QINGDAO
- ProductionCapacity: 200 Metric Ton/Day
- Purity: 93%
- Storage: Place at room temperature
- Transportation: FOB/CFR/CIF
- LimitNum: 1000 Kilogram
- Product Name: Hydrogenation catalyst
- appearance: Trilobe extrudates
- Particle size,mm: Ф1.5-2.5*2-10
- Crushing strength,N/cm: min150
- Bulk density, kg/L: 0.68-0.75
- Surface area,m2/g: min200
- Pore volume, mL/g: 0.40
- MoO3,wt%: 14.5-16.5
- CoO, wt%: 3.5-4.5
Superiority
Hydrogenation catalyst for prehydrogenation of high sulphur reforming material
The catalyst which has the advantage of high HDS, good compression resistance and abrasive resistance, low loading density, high space velocity and renewable use, takes modified alumina as carrier, with molybdenum and cobalt as the active components.
Application：It is mainly used for prehydrogenation of high sulphur reforming material and kerosene hydrogenation to produce aviation kerosene.
Details
Hydrogenation catalyst for prehydrogenation of high sulphur reforming material
The catalyst which has the advantage of high HDS, good compression resistance and abrasive resistance, low loading density, high space velocity and renewable use, takes modified alumina as carrier, with molybdenum and cobalt as the active components.
Application：It is mainly used for prehydrogenation of high sulphur reforming material and kerosene hydrogenation to produce aviation kerosene.
Physical-chemical properties:
|
item |
target |
item |
target |
|
appearance |
Trilobe extrudates |
Surface area,m2/g |
min200 |
|
Particle size,mm |
Ф1.5-2.5*2-10 |
Pore volume, mL/g |
0.40 |
|
Crushing strength,N/cm |
min150 |
MoO3,wt% |
14.5-16.5 |
|
Bulk density, kg/L |
0.68-0.75 |
CoO, wt% |
3.5-4.5 |
Activity index:
|
Process parameters |
Hydrogen partial pressure,Mpa |
temperature℃ |
Space velocity hr-1 |
Hydrogen to oil ratio,V/V |
|
1.6 |
270 |
8.0 |
80 |
|
|
Raw oil |
Iranian atmosphere distillation gasoline |
|||
|
Product oil |
sulfur max 0.5ppm,Nitrogen max0.5ppm |
|||
Packing: iron drums innerlining double-layer plastic bags.